| Resin PVC | SG3 | SG5 | SG8 | |
| Kelikatan, ml/g(atau nilai K) | 135-127 (72-71) 1350-1250 | 118-107 (68-66) 1100-1000 | 86-73 (59-55) 750-650 | |
| Bilangan zarah kekotoran≤ | 30 | 30 | 40 | |
| Kandungan meruap %, ≤ | 0.40 | 0.40 | 0.40 | |
| Ketumpatan muncul g/ml≥ | 0.42 | 0.45 | 0.45 | |
| Sisa Selepas Ayak | 0.25mm, ≦ | 2.0 | 2.0 | 2.0 |
| 0.063mm, ≥ | 90 | 90 | 90 | |
| Bilangan bijirin/400cm2≤ | 40 | 40 | 50 | |
| Nilai serapan plasticizer 100g resin g≥ | 25 | 17 | - | |
| Keputihan %,≥ | 75 | 75 | 70 | |
| Kekonduksian larutan pengekstrak air,【us/(cm.g)】≤ | 5 | - | - | |
| Baki kandungan klore tilena mg/kg≤ | 10 | 10 | 10 | |
| Baki Ethyidenedichlorideug/g | 150 | 150 | 150 | |
| RESIN PVC SG3 | ||||
| Perkara | spesifikasi | Ukur d Nilai | ||
| Gred Unggul | Gred pertama | Gred Berkelayakan | ||
| Nombor Kelikatan,ML/G | 127 ~ 135 | 127 ~ 135 | 127 ~ 135 | 131 |
| Pecahan jisim Jirim Meruap (termasuk air) | ≤0.3% | ≤0.4% | ≤0.5% | ≤0.2% |
| Ketumpatan Jelas, g/mL | ≥0.45 | ≥0.42 | ≥0.4 | ≥0.51 |
| Kurangkan onSieve, 250μmSieve mesh≤Sieve | 1.6% | 2% | 8% | 0.9% |
| Kurangkan onSieve, 63μmSieve mesh≥Sieve | 97% | 90% | 85% | 99% |
| “Mata Ikan”/400cm2≤ | 20 | 30 | 60 | 10 |
| Keputihan(160°C,10min)≥ | 78% | 75% | 70% | 83% |
| 100g Resin Penyerapan Plasticizer, g≥ | 26 | 25 | 23 | 27 |
| Nombor Zarah Kekotoran ≤ | 16 | 30 | 60 | 12 |
| Kekonduksian ekstrak air,uS/cm.g ≤ | 5 | 5 | --- | 0.6 |
| Kandungan Monomer Vinyl Klorida Baki,ug/g≤ | 5 | 5 | 10 | 1.6 |
| RESIN PVC SG5 | ||||
| Perkara | spesifikasi | Ukur d Nilai | ||
| Gred Unggul | Gred pertama | Gred Berkelayakan | ||
| Nombor Kelikatan,ML/G | 118 ~ 107 | 111.24 | ||
| Pecahan jisim Jirim Meruap (termasuk air) | ≤0.4% | ≤0.4% | ≤0.5% | ≤0.4% |
| Nombor zarah kekotoran ≤ | 16 | 30 | 80 | 16 |
| Ketumpatan Jelas, g/mL | ≥0.48 | ≥0.45 | ≥0.42 | ≥0.519 |
| Kurangkan onSieve, 250μmSieve mesh≤Sieve | 2% | 2% | 8% | 0.9% |
| Kurangkan onSieve, 63μmSieve mesh≥Sieve | 95% | 90% | 85% | 98% |
| “Mata Ikan”/400cm2≤ | 20 | 40 | 90 | 8 |
| Keputihan(160°C,10min)≥ | 78% | 75% | 70% | 81.39% |
| 100g Resin Penyerapan Plasticizer, g≥ | 19 | 17 | --- | 22.28 |
| Kandungan Monomer Vinyl Klorida Baki,ug/g≤ | 5 | 10 | 30 | 1 |
| RESIN PVC SG8 | |
| Perkara | spesifikasi |
| Nombor Kelikatan, ML/G | 73-86 |
| Nombor Zarah Kekotoran ≤ | 20 |
| Pecahan jisim Jirim Meruap (termasuk air) ≤ | 0.4% |
| Ketumpatan Jelas, g/mL≥ | 0.52 |
| Kurangkan onSieve, 250μmSieve mesh≤Sieve | 1.6% |
| Kurangkan onSieve, 63μmSieve mesh≥Sieve | 97% |
| “Mata Ikan”/400cm2≤ | 30 |
| 100g Resin Penyerapan Plasticizer, g≥ | 12 |
| Keputihan(160°C,10min)≥ | 75% |
| Kandungan Monomer Vinyl Klorida Baki,mg/l≤ | 5 |
Permohonan:
Bahagian dalam kereta, bahan hiasan keluarga, kotak lampu pengiklanan, tapak kasut, paip PVC, profil PVC, kepingan dan plat PVC, filem bergulung, mainan kembung, produk luar, wayar dan kabel PVC, kulit tiruan PVC, lantai kayu dan plastik, papan beralun , dan lain-lain.
PVC SG-3adalah untuk filem, hos, kulit, kabel wayar dan produk lembut tujuan am yang lain
PVC SG-5adalah untuk paip, kelengkapan, panel, kalendar, suntikan, pengacuan, profil dan sandal.
PVC SG-7/SG-8adalah untuk botol, kepingan, kalendar, suntikan tegar dan paip acuan.
Hak Cipta © Kumpulan Terkaya Hak Cipta Terpelihara
EN 
AR 
NL 
FR 
DE 
EL 
HI 
IT 
JA 
KO 
PL 
PT 
RO 
RU 
ES 
TL 
ID 
UK 
VI 
SQ 
MT 
TH 
TR 
FA 
AF 
MS 
SW 
KA 
UR 
BN 
LO 
NE 
SO 
TA 
ZU 
MY 
KK 
SI 
TG 
KU 
XH 